| dc.description | Anodizing merupakan proses pelapisan secara elektrolisis yang merubah aluminium menjadi aluminium oksida. Proses anodizing banyak digunakan dalam industri manufaktur khususya pada pemakaian komponen otomotif, karena banyak mempunyai keunggulan antara lain tahan terhadap goresan, mudah dalam perawatan dan menambah nilai dekoratif. Tujuan dari penelitian ini untuk mengetahui bagaimana pengaruh variasi waktu terhadap kekerasan dan ketebalan lapisan oksida dalam proses anodizing aluminium seri 6.
Spesimen dari plat aluminium seri 6, dimensi 50 mm x 30 mm x 9 mm. Spesimen di amplas dengan 3 kali proses pengamplasan menggunakan amplas logam seri P1000, P2000, dan C5000 yang dilanjutkan dengan proses cleaning dengan larutan natrium karbonat (Na2CO3). Dilanjutkan dengan proses etching, desmut, anodizing menggunakan konsentrasi larutan asam sulfat (H2SO4) 40% berbanding 60% air reverse osmosis. Variasi waktu yang digunakan pada proses pencelupan adalah 20 Menit, 30 Menit, 40 Menit, dengan arus listrik sebesar 2 Amper dan tegangan 24 Volt. Setelah itu dilakukan proses dyeing dan sealing. Pengujian yang dilakukan meliputi pengujian kekerasan (vikers) dan ketebalan lapisan oksida (coating thickness gauge).
Hasil dari pengujian kekerasan rata-rata yang terbentuk yaitu sebesar 108,3 VHN pada interval waktu pencelupan 20 menit, 112,4 VHN pada interval waktu pencelupan 30 menit, dan 112,9 VHN pada interval waktu 40 menit. Nilai kekerasan tertinggi sebesar 112,9 VHN didapat pada variasi waktu 40 menit, kemudian hasil pengujian ketebalan lapisan oksida menghasilkan ketebalan rata-rata lapisan 3,40 μm pada interval waktu 20 menit, 4,15 μm pada interval waktu 30 menit kemudian nilai ketebalan lapisan oksida tertinggi pada interval waktu pencelupan 40 menit adalah sebesar 5,07 μm. Dapat disimpulkan bahwa semakin lama waktu pencelupan pada proses anodizing mempengaruhi naiknya nilai kekerasan pada aluminium seri 6, kemudian semakin lama waktu pencelupan pada proses anodizing yang digunakan juga mempengaruhi naiknya ketebalan lapisan oksida yang tebentuk. | en_US |
| dc.description.abstract | Anodizing is an electrolytic coating process that converts aluminum into aluminum oxide. Anodizing process is widely used in manufacturing industry especially in the use of automotive components, because many have advantages such as resistant to scratches, easy to care and add decorative value. The purpose of this research is to know how the influence of time variation on hardness and thickness of oxide layer in anodizing aluminum series 6 process.
Specimens of aluminum plate 6 series, dimensions 50 mm x 30 mm x 9 mm. The specimen was sandpaper with 3 times sanding process using P1000, P2000 and C5000 series metal sandpaper followed by cleaning process with sodium carbonate (Na2CO3) solution. Followed by etching, desmut, anodizing process using concentration of sulfuric acid solution (H2SO4) 40% versus 60% reverse osmosis water. The time variations used in the dyeing process are 20 Minutes, 30 Minutes, 40 Minutes, with electric current of 2 Amper and 24 Volt. After that done dyeing and sealing process. Tests carried out include testing of hardness (vikers) and the thickness of the oxide layer (coating thickness gauge).
The results of the mean hardness testing were 108.3 VHN at 20 min intervals, 112.4 VHN at 30 minute dyeing intervals, and 112.9 VHN at 40 minute intervals. The highest hardness value of 112,9 VHN was obtained at 40 minute time variation, then the result of thickness testing of oxide layer yield average layer thickness 3,40 μm at interval time 20 minutes, 4,15 μm at time interval 30 minutes then coat thickness value The highest oxide at a time interval of 40 minutes was 5.07 μm. It can be concluded that the longer the dyeing time in the anodizing process influences the increase of hardness value on aluminum series 6, then the longer the dyeing time on the anodizing process used also affects the increase in the thickness of the oxide layer formed | en_US |
| dc.publisher | D3 UMY | en_US |
| dc.subject | Anodizing aluminum, Anodizing Time, Hardness, Oxide Coating. Anodizing aluminium, Waktu Anodizing, Kekerasan, Lapisan Oksida. | en_US |
| dc.title | PENGARUH WAKTU PENCELUPAN TERHADAP KEKERASAN PERMUKAAN DAN KETEBALAN LAPISAN OKSIDA HASIL ANODIZING ALUMINIUM SERI 6 | en_US |
| dc.type | Thesis