| dc.contributor.advisor | SOFIANI, ERNA | |
| dc.contributor.author | BILQIS AZIZAH, ASTRI | |
| dc.date.accessioned | 2018-10-08T04:11:16Z | |
| dc.date.available | 2018-10-08T04:11:16Z | |
| dc.date.issued | 2018-09-07 | |
| dc.identifier.uri | http://repository.umy.ac.id/handle/123456789/21853 | |
| dc.description | Penyebab kegagalan perawatan saluran akar ulang yang paling
dominan adalah obturasi yang tidak hermetis. Hal ini dapat dicegah dengan
penggunaan bahan sealer. Sealer yang memiliki ikatan yang baik dengan dinding
dentin yaitu sealer epoxy bis-phenol resin dan sealer Glass Ionomer Cement.
Bahan alami yang dapat melarutkan gutaperca pada perawatan saluran akar ulang
yaitu minyak kayu putih. Minyak kayu putih mempunyai efek antimikroba,
biokompatibel dan direkomendasikan untuk digunakan dalam perawatan saluran
akar ulang. Tujuan: Untuk mengetahui pengaruh sealer epoxy bis-phenol resin
dan Glass Ionomer Cement terhadap perlunakan gutaperca menggunakan cajuput
oil. Metode: Desain penelitian ini adalah eksperimental laboratoris murni.
Penelitian ini menggunakan 24 sampel blok akrilik saluran akar tunggal. Sampel
penelitian diberi perlakuan berbeda berupa jenis sealer yang digunakan dan lama
waktu inkubasi (15 hari, 22 hari, 29 hari). Data diolah dengan menggunakan oneway
ANOVA dan uji Post Hoc Tukey dengan tingkat kemaknaan 95% (p<0,05).
Hasil: Terdapat pengaruh sealer epoxy bis-phenol resin dan Glass Ionomer
Cement terhadap perlunakan gutaperca menggunakan cajuput oil. Hasil analisis
one-way ANOVA didapatkan nilai signifikansi 0,000 (p<0,05). Hasil analisi uji
Post Hoc menunjukan bahwa sealer epoxy bis-phenol resin yang didiamkan
selama 15 hari setelah berkontak dengan cajuput oil selama 5 menit memiliki nilai
perlunakkan lebih besar jika dibandingkan dengan sealer Glass Ionomer Cement
yang didiamkan selama 15 hari,22 hari dan 28 hari setelah berkontak dengan
cajuput oil selama 5 menit. Kesimpulan: Sealer epoxy bis-phenol resin lebih
mudah dibersihkan daripada sealer Glass Ionomer Cement dengan pelarut cajuput
oil. | en_US |
| dc.description.abstract | The most dominant cause of root canal treatment failure is nonhermetic
obturation. It could be prevented with the use of sealer material. The
sealer that has a good bond with the dentin wall is sealer epoxy bis-phenol resin
sealer and Glass Ionomer Cement. A natural material that could dissolve guttapercha
in root canal re-treatment is eucalyptus oil. The eucalyptus oil has an
antimicrobial effect, bio-compatible and recommended for use in root canal retreatment.
Objective: To determine the effect of epoxy bis-phenol resin sealer and
Glass Ionomer Cement sealer in softening the gutta-percha using cajuput oil.
Methods: The design of this study was pure laboratory experimental. This study
was using 24 samples of single root canal acrylic block. The samples were treated
differently by the type of sealer used and incubation time (15 days, 22 days, 29
days). The data were processed using one-way ANOVA and Post-Hoc Tukey test
with significance level 95% (p <0,05). Result: There was a significant effect of
epoxy bis-phenol resin sealer and Glass Ionomer Cement sealer in softening
gutta-percha using cajuput oil. The result of one-way ANOVA analysis obtained a
significance value of 0.000 (p <0,05). The results of Post-Hoc test analysis
showed that the resin sealer which was incubated for 15 days after contact with
cajuput oil for 5 minutes had a higher softening value compared to the Glass
Ionomer Cement sealer which was incubated for 15 days, 22 days and 28 days
after contacting with cajuput oil for 5 minutes. Conclusion: Sealer epoxy bisphenol
resin is easier to remove than Glass Ionomer Cement sealer with cajuput
oil solvent. | en_US |
| dc.subject | epoxy bis-phenol resin sealer, Glass Ionomer Cement sealer, Softening gutta-percha, Cajuput oil solvent | en_US |
| dc.title | PENGARUH SEALER EPOXY BIS-PHENOL RESIN DAN GLASS IONOMER CEMENT TERHADAP PERLUNAKAN GUTAPERCA MENGGUNAKAN CAJUPUT OIL | en_US |
| dc.type | Thesis
SKR
FKIK
269 | en_US |