| dc.description | Latar Belakang: Proses etsa asam pada saat pemasangan bracket ortodontik dan proses pelepasan bracket ortodontik seringkali menimbulkan demineralisasi di sekitar permukaan email. Novamin adalah mineral sintetis yang memiliki struktur mirip seperti mineral yang terkandung pada gigi.
Tujuan Penelitian: Untuk mengetahui potensi Novamin sebagai bahan remineralisasi dilihat dari kadar kandungan Unsur Ca, O, P dan kekasaran permukaan email.
Metode Penelitian: Dua puluh lima gigi dibagi menjadi lima kelompok (n= 5): I (kontrol), II (Biofix), III (Biofix+Novamin), IV (Fuji Ortho LC), dan V (Fuji Ortho LC+Novamin). Kekasaran permukaan diuji dengan menggunakan SR Tester KR 220. Kadar kandungan unsur di analisis dengan menggunakan EDX analysis dan perubahan pada permukaan email dilihat dengan menggunakan Scanning Electron Microscope.
Hasil: Terdapat perbedaan yang signifikan pada kadar kandungan unsur Ca dan P di semua kelompok. Kekasaran Permukaan juga menunjukkan perbedaan yang signifikan pada setiap kelompok. Perubahan pada permukaan email menunjukkan adanya prisma email yang terbuka, pits dan groves.
Kesimpulan: Novamin dapat meremineralisasi permukaan email yang memiliki demineralisasi. | en_US |
| dc.description.abstract | Background: Acid etching prior to orthodontic bracket bonding process and debonding bracket orthodontic may result enamel demineralization. Novamin is a synthetic mineral that structurally similar to tooth mineral composition.
Objective: To evaluate the effectiveness of Novamin on the amounts of Ca, O, P and the enamel surface roughness during remineralization process.
Method: Twenty five teeth were assigned to five groups (n= 5): I (control), II (Biofix), III (Biofix+Novamin), IV (Fuji Ortho LC), and V (Fuji Ortho LC+Novamin). Surface roughness was evaluated by SR Tester KR 220. Chemical composition was analyzed by EDX analysis and enamel surface changes by Scanning Electron Microscope.
Result: All groups showed differences amounts in Ca and P. Surface Roughness showed differences between all groups. Enamel surface changes included exposed prism, pits and groves.
Conclusion: Novamin showed significant remineralizing potential in enamel demineralization. | en_US |
| dc.publisher | FAKULTAS KEDOKTERAN DAN ILMU KESEHATAN UNIVERSITAS MUHAMMADIYAH YOGYAKARTA | en_US |
| dc.subject | Acid etching, Demineralization, Remineralization, Fuji Ortho LC, Biofix, Novamin | en_US |
| dc.title | PENGARUH PASTA GIGI YANG MENGANDUNG NOVAMIN TERHADAP PROSES REMINERALISASI PADA PERMUKAAN EMAIL SETELAH PELEPASAN BRACKET ORTODONTIK | en_US |
| dc.type | Thesis