| dc.description | Latar belakang : Material restorasi terus berkembang untuk menutupi
kekurangan dengan berbagai modifikasi. Restorasi yang diterima secara klinis
yaitu memiliki warna yang paling mirip dengan gigi asli dan memiliki stabilitas
warna jangka panjang. Perubahan warna pada restorasi gigi terutama pada gigi
anterior akan menurunkan rasa percaya diri seseorang. Salah satu contoh kasus
yang membutuhkan estetika sewarna gigi adalah restorasi kelas V, bahan restorasi
yang digunakan untuk kelas V diantaranya semen ionomer kaca konvensional,
RMGIC, dan kompomer.
Tujuan Penelitian: Untuk mengetahui pengaruh perendaman soft drink (Cocacola)
terhadap perubahan warna SIK konvensional, RMGIC, dan kompomer pada
restorasi kelas V.
Metode Penelitian: Jenis penelitian yang digunakan adalah eksperimental
laboratoris murni. Sampel yang digunakan berjumlah 27 gigi yang dibagi menjadi
3 kelompok, sampel dipreparasi membentuk kavitas kelas V. Kelompok I akan
direstorasi dengan SIK konvensional (GC Fuji II A3), kelompok II akan
direstorasi dengan menggunakan RMGIC (GC Fuji II LC A3), dan kelompok III
akan direstorasi menggunakan kompomer (Dyract eXtra A3). Kemudian sampel
direndam di dalam Coca-cola selama 7 hari. Nilai warna sampel diukur sebelum
dan sesudah perendaman menggunakan Spektrofotometer UV- 2401 PC
(SHIMADZU).
Hasil Penelitian: Ketiga kelompok bahan restorasi yang diuji masing-masing
menunjukkan perubahan warna yang signifikan setelah direndam pada soft drink
(Coca-cola). SIK konvensional menunjukkan perubahan warna yang paling tinggi,
sedangkan kompomer menujukkan perubahan warna yang paling rendah.
Kesimpulan: Terdapat pengaruh soft drink (Coca-cola) terhadap perubahan warna
SIK konvensional, RMGIC, dan kompomer. | en_US |
| dc.description.abstract | Background: Restoration material keeps developing to cover some lacks with
various modifications. Restoration that is clinically accepted has the most similar
color with real teeth and has a long-term stability. The color changes in teeth
restoration especially in anterior teeth will decrease one’s confidence. One of the
cases that needs dental aesthetics is class V restoration. The materials used for
class V are conventional GIC, RMGIC, and compomer.
Research Objective: To find out the influence of soft drink (Coca-cola) toward the
color changes of conventional GIC, RMGIC, and compomer in class V
restoration.
Research Method: Research type used was pure laboratory experimental design.
The samples used were 27 teeth divided into 3 groups. The samples were prepared
to form cavity class V. Group I would be restored using conventional GIC (GC
Fuji II A3), group II would be restored using RMGIC (GC Fuji II LC A3), and
group III would be restored using compomer (Dyract eXtra A3). Then, the
samples were immersed in Coca-cola for 7 days. The value of sample color was
measured before and after the immersion using Spectrophotometer UV-2401 PC
(SHIMADZU).
Research Result: The three groups of restoration materials tested show
significant color changes respectively after being immersed in soft drink (Cocacola).
Conventional GIC shows the highest color change while compomer shows
the lowest color change.
Conclusion: There is influence of soft drink (Coca-cola) toward the color chages
of conventional GIC, RMGIC, and compomer. | en_US |
| dc.publisher | FAKULTAS KEDOKTERAN DAN ILMU KESEHATAN UNIVERSITAS MUHAMMADIYAH YOGYAKARTA | en_US |
| dc.subject | class V restoration, conventional GIC, RMGIC, compomer, soft drink (Coca-cola), color changes | en_US |
| dc.title | PENGARUH SOFTDRINK TERHADAP PERUBAHAN WARNA PADA TUMPATAN KELAS V MENGGUNAKAN SIK KONVENSIONAL, RMGIC DAN KOMPOMER | en_US |