| dc.contributor.advisor | DWI ATMAJA, WIDYAPRAMANA | |
| dc.contributor.author | RIZKI WIDIANDRI, BELA | |
| dc.date.accessioned | 2018-10-10T03:38:47Z | |
| dc.date.available | 2018-10-10T03:38:47Z | |
| dc.date.issued | 2018-06-08 | |
| dc.identifier.uri | http://repository.umy.ac.id/handle/123456789/22018 | |
| dc.description | FRC merupakan suatu bahan kombinasi terdiri dari matriks polimer dan
reinforced fiber. Reinforced fiber berfungsi untuk menyalurkan beban yang
diterima komposit serta dapat meningkatkan sifat mekanis pada FRC salah
satunya adalah kekuatan fleksural. Penempatan posisi fiber pada zona tension dan
mikroporositas pada FRC dapat mempengaruhi kekuatan fleksural. Penelitian ini
bertujuan untuk mengetahui pengaruh posisi fiber polyethylene pada zona tension
dan mikroporositas terhadap kekuatan fleksural FRC (Packable Resin Composite).
Penelitian ini merupakan jenis penelitian eksperimental laboratoris murni.
Bahan penelitian menggunakan fiber polyethylene lebar 2mm, Filtek Z250 XT
packable, silane dan saliva buatan. Sampel berupa batang polyethylene fiber
reinforced composite (FRC) dengan ukuran 25x2x2mm dan fiber berada pada
zona tension dengan ketebalan 0,2 mm dan keseluruhan ketebalan packable resin
composite 1,8 mm. Pengaplikasian resin dilakukan dengan teknik kondensasi
manual menggunakan kondensor dan glass slide. Sampel yang telah dibuat
diamati menggunakan SEM untuk mengetahui mikroporositas, kemudian
direndam dalam saliva buatan dan disimpan di dalam inkubator pada temperatur
37°C selama 24 jam. Sampel diuji dengan UTM untuk mengetahui kekuatan
fleksural dengan beban awal 1 Newton dan titik tumpu pada sampel sebesar 2
mm.
Hasil mikroporositas dan kekuatan fleksural yang dianalisa secara statistik
dengan uji One Way Anova (p=0,000). Hasil penelitian menunjukkan dengan nilai
rerata mikroporositas 1,68 mm2 maka kekuatan fleksural FRC sebesar 99,32 Mpa.
Hasil ini menunjukkan terdapat pengaruh secara signifikan (p<0,05). Kesimpulan
dari penelitian ini adalah semakin rendah nilai mikroporositas maka kekuatan
fleksural yang dimiliki akan semakin tinggi dan sebaliknya. | en_US |
| dc.description.abstract | FRC is a combination material of polymer matrix and reinforced fiber.
Reinforced fiber serves to distribute the load from the matrix to the fibers and it
can improve the mechanical properties of FRC (flexural strength). The position of
fiber on tension zone and the microporosity has an important influence of FRC
flexural strength. The aim of this study was to determine effect of polyethylene
fiber position (tension zone) and the microporosity on FRC flexural strength
(Packable Resin Composite).
This study was an experimental research laboratory. Materials research
used Polyethylene fiber 2mm width, Filtek Z250XT Packable, silane, and artificial
saliva. The sample in this study were the polyethylene fiber reinforced composite
(FRC) with 25x2x2mm and the fiber is in the tension zone of 0.2 mm thickness and
the entire thickness of packable resin composite is 1.8 mm. Resin was applied by
manual condensation technique using condenser and glass slide. The samples
were observed using SEM to determine the microporosity then the samples were
immersed in artificial saliva and incubated at 37°C for 24 hours. The samples
were tested using UTM to determine the flexural strength with the 1 Newton
initial load and the fulcrum of the sample is 2 mm.
The results of statistical test of microporosity and flexural strength by
using One Way Anova method (p=0,000). The result show the average value of
FRC microporosity is 1,68 mm2 then the FRC flexural strength is 99,32 Mpa.
These results show a significant effect (p <0.05). The conclusion of this research
is the lower value of microporosity then the flexural strength will be higher and
vice versa. | en_US |
| dc.publisher | FAKULTAS KEDOKTERAN DAN ILMU KESEHATAN UNIVERSITAS MUHAMMADIYAH YOGYAKARTA | en_US |
| dc.subject | flexural strength, microporosity, tension zone, fiber reinforced composite | en_US |
| dc.title | PENGARUH POSISI FIBER POLYETHYLENE PADA ZONA TENSION DAN MIKROPOROSITAS TERHADAP KEKUATAN FLEKSURAL FRC (PACKABLE RESIN COMPOSITE) | en_US |
| dc.type | Thesis
SKR
FKIK
238 | en_US |