| dc.description | Plastik ABS (Akrilonitril-Buadiena-Stirena) adalah sejenis kopolimer yang tersusun dari beberapa monomer pembentuk. ABS memiliki sifat stabil terhadap panas, memiliki kekuatan tinggi, mempunyai sifat ketahanan pukul, sifat kekerasan, kaku dan mudah diproses, liat, keras, dapat direkatkan, tahan korosi dan dapat diproses elektroplating. Plastik ABS adalah salah satu polimer yang paling serng digunakan dibidang industri seperti elektronik, otomotif dan peralatan rumah tangga. Penelitian ini bertujuan untuk mengetahui dan menganalisa pengaruh suhu electrolessplating terhadap karakteristik fisik yang meliputi ketebalan, kekasaran, dan mekanik yang meliputi kekerasan dan keausan.
Metode elektrolessplating digunakan untuk mengatasi kelemahan plastik ABS. Pada penelitian ini ABS dengan dimensi panjang 80 mm, lebar 7 mm, dan tebal 3 mm diberi perlakuan elektroless plating dengan zat pelapis nikel. Variabel penelitian yang digunakan dalam penelitian ini adalah variasi suhu elektroless pelapisan nikel dengan variasi 40oC, 50oC, 60oC, 70oC. Variabel uji yang dilakukan adalah uji karakteristik fisik yang meliputi pengujian mikro, pengujian SEM, pengujian ketebalan, pengujian kekasaran, dan mekanik yang meliputi pengujian kekerasan dan pengujian keausan.
Hasil penelitian menunjukan bahwa ketebalan lapisan nikel meningkat pada suhu 50oC dan mengalami penurunan pada suhu 60oC dan 70oC. Pada uji kekasaran, kekasaran spesimen meningkat seiring dengan meningkatnya suhu elektroless dengan suhu secara berurutan 40oC, 50oC, 60oC, 70oC dan dengan nilai kekasaran secara berurutan 0,170 μm, 0,192 μm, 0,255 μm 0,422 μm. Pada pengujian kekerasan nilai kekerasan tidak terjadi peningkatan yaitu dengan nilai kekerasan tertinggi 84,5 sedangkan nilai kekerasan pada raw material sebesar 83,5. Sementara laju keausan dari lapisan nikel pada suhu elektroless plating 40oC, 50oC, 60oC, 70oC secara berutuan adalah sebesar 19,01, 13,00, 8,80, dan 4,19. | en_US |
| dc.description.abstract | ABS (Acrylonitrile-Buadiene-Styrene) plastic is a type of copolymer composed of several forming monomers. ABS have a properties that heat resistant stable, has high strength, has an endurance, hardness, rigidity and is easy to process, clay, hard, can be bonded, corrosion resistant and can be electroplated. ABS plastic is one of the most effective polymers used in industries such as electronics, automotive and household appliances. This study aims to determine and analyze the effect of electrolessplating temperature on physical characteristics including thickness, roughness, and mechanics which include hardness and wear.
Electrolessplating methods are used to overcome the disadvantages of ABS plastics. In this study ABS with dimensions of 80 mm in length, 7 mm in width, and 3 mm in thickness was given electrolessplating treatment with nickel coating. The research variable used in this study is the electrolyte temperature variation of nickel coating with variations of 40oC, 50oC, 60oC, 70oC. The test variables carried out are physical characteristics which include micro testing, SEM testing, thickness testing, roughness testing, and mechanics which include hardness testing and wear testing.
The results showed that the thickness of the nickel layer increased at 50oC and decreased at 60oC and 70oC.In the roughness test, the roughness of the specimens increased with increasing electrolyte temperature with temperature sequentially 40oC, 50oC, 60oC, 70oC and with a roughness value of 0,170 μm, 0,192 μm, 0,255 μm 0,422 μm.In the hardness test, the hardness value did not increase with the highest hardness value of 84.5 while the hardness value in the raw material was 83.5.While the wear rate of the nickel layer at electrolytic plating temperatures of 40oC, 50oC, 60oC, 70oC in order was 19.01, 13.00, 8.80, and 4.19 | en_US |
| dc.publisher | FAKULTAS TEKNIK UNIVERSITAS MUHAMMADIYAH YOGYAKARTA | en_US |
| dc.subject | elektroless nickel plating, ABS plastic, temperature of eletroless | en_US |
| dc.title | PENGARUH VARIASI SUHU ELECTROLESSPLATING NIKEL TERHADAP KARAKTERISTIK FISIK DAN MEKANIK PADA PLASTIK ABS | en_US |