| dc.description | Nikel krom merupakan zat kimia yang dapat digunakan sebagai bahan pelapis untuk meningkatkan kualitas materialnya. Untuk meningkatkan kualitasnya maka dilakukan perlakuan permukaan dengan metode proses electroplating-nickel chrom. Tujuannya untuk melapisi permukaan materialnya sehingga lebih tebal dan kokoh.
Penelitian ini menggunakan spanner tower sebagai bahan yang akan dilapisi nikel krom. Variabel yang digunakan adalah waktu dengan variasi 40 menit dan waktu 60 menit. Pengujian yang dilakukan adalah uji kekasaran dengan menggunakan alat Surface Roughness Tester DR220 dan pengukuran ketebalan menggunakan alat Microscope Olympus BX53M.
Berdasarkan hasil penelitian diperoleh nilai kekasaran yang menurun seiring dengan bertambahnya waktu, yaitu pada variasi waktu 40 menit memiliki kekasaran rata-rata sebesar 0.042 μm dan pada variasi waktu 60 menit memiliki kekasaran rata-rata sebesar 0.032 μm. Ketebalan untuk spanner tower juga meningkat seiring dengan bertambahnya variasi waktu, yaitu pada variasi waktu 40 menit ketebalan permukaan bagian luar yang terjadi sebesar 68.88 μm dan ketebalan permukaan bagian dalam yang terjadi sebesar 44.28 μm. Sedangkan pada variasi waktu 60 menit ketebalan permukaan bagian luar yang terjadi sebesar 99.62 μm dan ketebalan permukaan bagian dalam yang terjadi sebesar 51.37 μm. Dari data hasil penelitian dapat disimpulkan bahwa penambahan waktu krom berpengaruh pada menurunnya kekasaran dan bertambahnya ketebalan benda. | en_US |
| dc.description.abstract | Chrome nickel is a chemical that can be used as a coating material to improve the quality of the material. To improve its quality, surface treatment is carried out with the electroplating-nickel chrom process method. The goal is to coat the surface of the material so that it is thicker and stronger.
This research uses tower spanner as material to be coated with chrome nickel. The variables used are time with a variation of 40 minutes and 60 minutes. The tests performed were roughness tests using Surface Roughness Tester DR220 and thickness measurements using the Olympus BX53M Microscope.
Based on the results of the study, it was found that the roughness value decreases with increasing time variation, that is, in the variation of time 40 minutes has an average roughness of 0.042 μm and at 60 minutes the variation has an average roughness of 0.032 μm. The thickness for the tower spanner also increases with increasing time variation, which is at a variation of 40 minutes the outer surface thickness that occurs is 68.88 μm and the inner surface thickness that occurs is 44.28 μm. Whereas in the time variation of 60 minutes the outer surface thickness that occurs is 99.62 μm and the inner surface thickness that occurs is 51.37 μm. From the results of the research data it can be concluded that the addition of time variations in chrome has an effect on decreasing roughness and increasing the thickness of the object. | en_US |
| dc.publisher | FAKULTAS TEKNIK UNIVERSITAS MUHAMMADIYAH YOGYAKARTA | en_US |
| dc.subject | chrome nickel, tower spanner, time variation, roughness, thickness | en_US |
| dc.title | PERBANDINGAN ELEKTROPLATING PADA CAST IRON UNTUK SPANER TOWER DENGAN PERLAKUAN PELAPISAN NICKEL CROME DAN GALVANIS | en_US |
| dc.type | Thesis
SKR
FT
257 | en_US |