| dc.description.abstract | Electroplating is a metal coating process that utilizes electrical energy as
a source of coating energy with an anode which will dissolve into electrolyte fluid
and will then attach to the cathode, currently the electroplating process is very
widely used and its development is very rapid. Electroplating process will increase
thickness, hardness and corrosion resistance of coated objects.
The material in this study is the drum brake bushings and the coating
process carried out on the bushings will use variations in voltage and time, a
variation of 1.8V with a length of 30 minutes and 2.3V with a length of 40 minutes.
In this study used several tests namely thickness, hardness and corrosion testing.
The results of the study show that the voltage and time of immersion used
greatly affect the thickness value, the hardness of the corrosion rate of the bushings,
the greatest thickness value is in the variation of 2.3V with a 40 minute immersion
time with a thickness value of 54.41 μm and the smallest thickness value in the
variation of 1, 8V with a dipping time of 30 minutes with a thickness value of 9.55
μm, the hardness values obtained from the two variations also showed different
results at variations of 2.3V with 40 minutes obtained a hardness value of 536.6 HV
compared with a variation of 1.8V with time 30 minutes with the hardness value
obtained 442.3 HV, the two results of violence is very far when compared to objects
without coating which only has a hardness value of 247.6 HV. From this study also
obtained corrosion test results with the salt spray test method with ASTM B117-16
standard with a 12-hour test time obtained corrosion values during the test time of
2% on each variation. | en_US |
| dc.publisher | FAKULTAS TEKNIK UNIVERSITAS MUHAMMADIYAH YOGYAKARTA | en_US |
| dc.subject | Electroplating, bushing drum brake, thickness, hardness, salt spray test | en_US |
| dc.title | PENGARUH TEGANGAN DAN WAKTU PROSES ELECTROPLATING BUSHING DRUME BRAKE TERHADAP KETEBALAN KEKERASAN DAN KETAHANAN KOROSI | en_US |
| dc.type | Thesis SKR FT 694 | en_US |