| dc.description | Latar Belakang : Bleaching merupakan perawatan diskolorasi gigi yang paling konservatif. Restorasi tambahan seperti veneer direk komposit biasa diaplikasikan untuk menyempurnakan estetika gigi pasca bleaching. Bleaching menghasilkan residu berupa radikal bebas yang dapat menghambat polimerisasi bonding dan membuat perlekatan komposit pada gigi pasca bleaching menurun. Penelitian ini bertujuan untuk mengetahui perbedaan efektivitas larutan ekstrak buah jambu biji (Psidium guajava L.) 10%, 20%, dan 40% sebagai bahan antioksidan alami dalam meningkatkan perlekatan veneer direk resin komposit terhadap gigi pasca bleaching.
Metode : Penelitian ini menggunakan desain penelitian eksperimental murni laboratoris dengan desain studi cross-sectional. Sampel penelitian berjumlah 20 gigi premolar permanen yang diambil secara acak dari puskesmas dan klinik gigi di wilayah Magelang-Yogyakarta. Sampel diseleksi menurut kriteria inklusi dan kriteria eksklusi yang telah ditetapkan. Sampel kemudian dibagi ke dalam empat kelompok, yaitu : kelompok kontrol, kelompok larutan ekstrak jambu biji 10%, 20%, dan 40%. Kekuatan perlekatan komposit diukur melalui uji geser dengan alat Universal Testing Machine (UTM) merk Pearson Panke Equipment Ltd, UK. Data hasil penelitian dianalisis dengan uji statistik parametrik One Way ANOVA dan uji Post Hoc dengan Least Significant Difference (LSD).
Hasil : Nilai tegangan geser pada kelompok kontrol, kelompok larutan ekstrak jambu biji 10%, 20%, dan 40% berturut-turut adalah 1,33±0,42 MPa, 3,0±1,06 MPa, 2,11±0,61 MPa, dan 1,94±0,65 MPa. Nilai tegangan geser pada kelompok larutan ekstrak jambu biji 10% berbeda signifikan dibandingkan dengan tegangan geser pada ketiga kelompok lainnya dengan nilai signifikansi 0,002 (p<0,05). Nilai tegangan geser pada kelompok kontrol, kelompok larutan ekstrak jambu biji 20%, dan 40% tidak menunjukkan perbedaan yang signifikan.
Kesimpulan : Larutan ekstrak jambu biji 10% merupakan bahan antioksidan alami yang paling efektif dalam meningkatkan perlekatan veneer direk komposit pasca bleaching menggunakan hidrogen peroksida 40%. | en_US |
| dc.description.abstract | Background : Bleaching is the most conservative treatment for discolored teeth. Direct composite veneer usually placed to improve aesthetic after bleaching. In direct composite veneer treatment, presence of free radicals residual after bleaching can inhibit the polymerization of bonding agent and decrease composite shear bond strength. This study aimed to evaluate the differences in effectiveness of 10%, 20%, and 40% guava (Psidium guajava L.) extract solution as natural antioxidant agent to improve shear bond strength of direct composite veneer to bleached enamel.
Method : In this cross sectional study design, 20 extracted premolar permanent teeth were randomly colected from dental clinic and PHC around Magelang-Yogyakarta. All of the sample were selected based on exclusion and inclusion criteria. Then, the teeth were divided into four groups as follows : control group, 10%, 20%, and 40% guava extract solution group. Composite shear bond strength was measured by using Pearson Panke Equipment, Ltd Universal Testing Machine (UTM). Data were analyzed using One Way ANOVA followed by Least Significant Difference (LSD) Post Hoc test.
Result : The result show that shear bond strength of control group, 10%, 20%, and 40% guava extract solution group scores were 1,33±0,42 MPa, 3,0±1,06 MPa, 2,11±0,61 MPa, and 1,94±0,65 MPa respectively. Significant highest shear bond strength values was observed in 10% guava extract solution group with significant score was 0,002 (p<0,05). There were no significant shear bond strength in control group, 20%, and 40% guava extract solution group.
Conclussion : 10% guava extract solution was the most effective natural antioxidant agent to improve shear bond strength of direct composite veneer to bleached enamel with 40% hydrogen peroxide. | en_US |
| dc.publisher | FAKULTAS KEDOKTERAN DAN ILMU KESEHATAN UNIVERSITAS MUHAMMADIYAH YOGYAKARTA | en_US |
| dc.subject | Psidium guajava L., guava extract, bleaching, direct composite veneer | en_US |
| dc.title | PERBEDAAN EFEKTIVITAS LARUTAN EKSTRAK JAMBU BIJI 10%, 20%, DAN 40% SEBAGAI BAHAN ANTIOKSIDAN ALAMI TERHADAP PERLEKATAN VENEER DIREK RESIN KOMPOSIT PASCA BLEACHING | en_US |
| dc.type | Thesis