| dc.description | Frame merupakan komponen pembentuk sepeda yang paling penting karena mempengaruhi karakteristiknya. Salah satu faktor utama yang mempengaruhi frame adalah material penyusun frame. Material penyusun frame sepeda biasanya terbuat dari steel, chromoly, aluminium alloy, dan titanium. Serat carbon aramid adalah material yang jauh lebih ringan dari pada material yang lainnya. Carbon Aramid memiliki massa jenis sebesar 1,44 g/cm³ sedangkan aluminium alloy yang biasa digunakan untuk aplikasi frame sepeda memiliki massa jenis sebesar 2,70 g/cm³. Keuntungan serat carbon aramid yang lainnya yaitu kekuatan tinggi, anti korosi dan peredam getaran. Penelitian ini membuat tabung komposit serat carbon aramid untuk aplikasi frame sepeda dengan uji kuat tarik dan kuat tekan dengan variasi curing dan post curing.
Pembuatan komposit tabung karbon aramid/epoxy menggunakan metode hand lay-up. Pengujian yang dilakukan yaitu uji tarik mengacu pada ASTM D 638-4. Penelitian ini menggunakan 6 lapisan serat karbon kevlar dan variasi parameter curing pada temperatur 100°C, 120°C, 150°C selama 60 menit dan post curing pada temperatur 100°C, 120°C, 150°C selama 60 menit.
Dari hasil penelitian diperoleh bahwa variasi parameter curing dan post curing mempengaruhi besar nilai kuat tekan dan tarik. Nilai rata-rata kuat tekan variasi curing tertinggi diperoleh pada temperatur 150°C sebesar 558 Mpa. Sedangkan nilai rata-rata kuat tekan variasi post curing tertinggi diperoleh pada temperatur 150°C sebesar 598 Mpa. Nilai rata-rata kuat tarik variasi curing tertinggi diperoleh pada temperatur 150°C sebesar 328,13 Mpa, sedangkan untuk nilai rata-rata kuat tarik variasi post curing tertinggi diperoleh pada temperatur 150°C sebesar 413,88 Mpa. | en_US |
| dc.description.abstract | Frame is a bike component of the most important because it affects the characteristics. One of the main factors that affect the frame is the material making up the frame. Material constituent bicycle frames are usually made of steel, chromoly, aluminum alloy, and titanium. Aramid carbon fiber is a material that is much lighter than other materials. Carbon Aramid has a density of 1.44 g/cm³ while the aluminum alloy used for the application of a bicycle frame has a density of 2.70 g/cm³. Advantages of carbon fiber aramid others are high strength, anti-corrosion and vibration damping. This study makes aramid composite tubes of carbon fiber bicycle frames with the applications for tensile strength and compressive strength with a variety of curing and post curing.
Carbon tube composite manufacture aramid / epoxy using hand lay-up method. Tests done of the tensile test referring to ASTM D 638-4. This study uses six layers of kevlar and carbon fiber parameter variations curing at 100 ° C, 120 ° C, 150 ° C for 60 minutes and post curing at 100 ° C, 120 ° C, 150 ° C for 60 minutes.
The result showed that variations in curing and post curing parameters affect the compressive strength and tensile values. The average value of the compressive strength of the highest curing variation obtained at a temperature of 150 ° C for 558 Mpa. While the average value of the compressive strength of the highest variation obtained post curing at 150 ° C for 598 Mpa. The average value of variations in curing highest tensile strength obtained at a temperature of 150 ° C for 328.13 Mpa, while the average value of the tensile strength variation highest post curing obtained at 150 ° C for 413.88 Mpa. | en_US |
| dc.publisher | FAKULTAS TEKNIK UNIVERSITAS MUHAMMADIYAH YOGYAKARTA | en_US |
| dc.subject | Carbon aramid, curing, post curing, tensile test, compression test. | en_US |