| dc.description | Kaca FTO yang digunakan sebagai substrat kaca DSSC harus memiliki sifat optik yang tinggi. Proses pembuatan kaca FTO dengan menggunakan metode temperatur sintering dan ionisasi larutan karena metode ini sederhana dan biaya yang relatif rendah. Kaca FTO ini dibuat dengan bahan baku timah (II) klorida hidrat sebagai prekursor, amonium florida sebagai doping dan etanol 99% sebagai pelarut. Sifat optik yang dihasilkan dipengaruhi oleh temperatur sintering dengan varisasi 400oC, 450oC, 500oC, 550oC dan ketinggian jarak cerobong pengionisasi dengan variasi 1 cm dan 1,5 cm. Hasil penelitian ini menunjukan bahwa semakin tinggi temperatur sintering maka akan semakin kecil nilai konduktivitas dan nilai trasmitansi dan semakin tinggi ketinggian jarak cerobong pengionisasi maka akan semakin kecil nilai konduktivitas dan akan semakin tinggi nilai transmitansi. Pada penelitian ini sifat optik kaca FTO yang tinggi diperoleh pada temperatur sintering 400oC dan ketinggian jarak cerobong pengionisasi 1 cm dengan nilai resistivitas 26,72 .cm dan nilai trasmitansi 80,46%. | en_US |
| dc.description.abstract | FTO glass that used as substrate DSSC glass must have high optical characteristic. Process of making the FTO glass by using sintering temperature method and solution ionization because this method was simple and relatively low cost. This FTO glass made by tin (II) chloride hydrate as precursor, ammonium florid as a doping and ethanol 99% as solvent. The result of optical characteristic was influenced by sintering temperature with the variation 400oC, 450oC, 500oC, 550oC and altitude of ionization chimney with the variation 1 cm and 1,5 cm The results of this research showed that the higher the sintering temperature the smaller the conductivity value and the transmittance value and the higher the distance of the ionization chimney the smaller the conductivity value and the higher the transmittance value. In this research, the high optical characteristic of FTO glass were obtained at sintering temperature of 400oC and height of ionization chimney distance 1 cm with resistivity value 26,72 .cm and transmittance value 80,64%. | en_US |
| dc.publisher | PROGRAM VOKASI UNIVERSITAS MUHAMMADIYAH YOGYAKARTA | en_US |
| dc.subject | the optical characteristic FTO glass, sintering temperature, resistivity, transmittance | en_US |
| dc.title | ANALISIS PENGARUH VARIASI TEMPERATUR SINTERING DAN KETINGGIAN JARAK CEROBONG PENGIONISASI TERHADAP SIFAT OPTIK KACA FTO | en_US |