| dc.description | Seiring berkembangnya teknologi khususnya dibidang struktur, penggunaan beton
masih menjadi salah satu pilihan untuk bahan struktur. Beton masih menjadi pilihan
utama bahan elemen struktur bangunan, dikarenakan keunggulan beton yakni dari
segi kekuatan, tahan terhadap api, bahan penyusun yang mudah didapat dan dari
segi harga yang murah. Beton mutu tinggi dibutuhkan pada jembatan dan gedung
bertingkat tinggi. Beton mutu tinggi dapat diperoleh dengan cara menambahkan
superplasticizer. Fungsi superplasticizer untuk memudahkan proses pengerjaan
dan meningkatkan mutu beton. Tujuan penelitian ini adalah untuk mengetahui kuat
tekan beton mutu tinggi dengan variasi merk bahan tambah superplasticizer pada
umur 7 hari, 14 hari dan 28 hari. Pembuatan benda uji mengacu pada American
Concrete Institute Method. Benda uji yang digunakan berbentuk silinder memiliki
dimensi 15 cm x 30 cm. Hasil penelitian didapatkan bahwa pada umur 7 hari variasi
merk Bestmittel didapat nilai rata–rata tertinggi sebesar 40,47 MPa, pada umur 14
hari variasi merk Viscocrete 1003 didapat nilai rata–rata tertinggi sebesar 45,06
MPa dan pada umur 28 hari variasi merk Viscocrete 1003 didapat nilai rata–rata
tertinggi sebesar 46,58 MPa. | en_US |
| dc.description.abstract | Along with the development of technology, especially in the field of structure.
Concrete is still the main choice of building structural elements, because of the
superiority of concrete in strength, fire resistance, easy obtain constituent materials
and low price. Hight quality concrete is needed on bridges and high-rise buildings.
Hight strength concrete can be obtained by adding superplasticizer. The function
of the superplasticizer is to facilitate the process of work as well as to improve the
quality of the concrete. The purpose of this study was to determine the compressive
strength of high quality concrete with a variety of brands of ingredients added
superplasticizers at the age of 7 days, 14 days and 28 days. Making test specimens
refers to the American Concrete Institute Method. The research uses a cylindrical
test objects 15 cm x 30 cm. The results showed that at the age of 7 days the
Bestmittel brand variation obtained the highest average value of 40.47 MPa, at the
age of 14 days the variety of Viscocrete 1003 brands obtained the highest average
value of 45.06 MPa and at the age of 28 days the Viscocrete brand variation 1003
obtained the highest average value of 46.58 MPa. | en_US |
| dc.publisher | FAKULTAS TEKNIK UNIVERSITAS MUHAMMADIYAH YOGYAKARTA | en_US |
| dc.subject | high strength concrete, superplasticizer, viscocrete 1003, sikament NN, bestmittel, concrete compressive strength. | en_US |
| dc.title | KUAT TEKAN BETON MUTU TINGGI DENGAN VARIASI MERK BAHAN TAMBAH SUPERPLASTICIZER | en_US |