| dc.contributor.advisor | RAHMAN, MUHAMMAD BUDI NUR | |
| dc.contributor.advisor | HIMAROSA, RELA ADI | |
| dc.contributor.author | PRANAWA, FURQON NAZHIF | |
| dc.date.accessioned | 2019-11-11T01:41:16Z | |
| dc.date.available | 2019-11-11T01:41:16Z | |
| dc.date.issued | 2019-10-17 | |
| dc.identifier.uri | http://repository.umy.ac.id/handle/123456789/30314 | |
| dc.description | Elektroplating merupakan salah satu proses plelapisan bahan padat dengan
lapisan logam menggunakan bantuan arus listrik melalui suatu elektrolit. Benda yang
dilakukan pelapisan harus merupakan konduktor atau dapat menghantarkan arus
listrik. Elektroplating ditujukan untuk berbagai keperluan mulai dari perlindungan
terhadap karat seperti pada pelapisan pada besi baja yang dipergunakan buat banyak
sekali keperluan. Pelapisan nikel serta krom umumnya ditujukan untuk menjadikan
benda memiliki permukaan lebih keras dan mengkilap selain juga menjadi
pelindungan terhadap korosi.
Adjuster Chain di bagian arm motor yang berfungsi untuk mengencangkan
rantai. Mwmiliki nilai keindahan yang kurang, maka dari itu dilakukan proses
Elektroplating agar menambah nilai dekoratif dari suatu logam dan dilakuakan
penelitian tentang pelapisan nickel-chrome untuk mengetahui bagaimana pengaruh
posisi pencelupan selama proses elektroplating terhadap sifat fisis dan mekanis hasil
pelapis. Dimana pada Spesimen A permukaannya menghadap langsung dengan anoda
dan Spesimen B permukaannya menyampingi anoda dan dilakukan pengujian
ketebelan, kekasaran, ketahanan korosi.
Hasil ketebalan yang paling baik dan paling tebal didapat pada spesimen A
segmen 1 dengan nilai ketebalan 27,91 μm, dibanding dengan ketebalan pada
spesimen B segmen 1 dengan nilai ketebalan 19,89 μm. Pada posisi pencelupan
dengan variasi permukaan spesimen menghadap langsung dengan anoda memiliki
nilai kekasaran yang sangat tinggi dengan nilai rata – rata 2,08 μm dibandingakan
variasi pencelupan pada permukaan spesimen yang menyampingi anoda mempunyai
nilai kekasaran yang relatif lebih kecil dengan nilai rata – rata 1,07 μm. Ketahan
korosi yang terjadi pada Adjuster Chain memiliki presentase ketahanan korosi yang
sama yaitu sebesar 2 % dari kedua variasi. Dengan menggunakan variasi pencelupan
yang berbeada ternyata tidak ada pengaruh terhadap ketahanan korosi. | en_US |
| dc.description.abstract | Electroplating is the process of coating a solid material with a metal layer
using the help of an electric current through an electrolyte. The coated object must be
a conductor or can conduct electricity. Electroplating is intended for various
purposes ranging from protection against rust such as coatings on steel used for
various purposes. Nickel and chrome plating are generally intended to make objects
have a harder and shiny surface as well as corrosion protection.
Adjuster Chain on the arm motor that serves to tighten the chain. Having a
beauty value that is lacking, the coating process is carried out to increase the
decorative value of the metal and a nickel-chrome coating study is carried out to find
out how the effect of the dyeing position during the coating process on the physical
and mechanical properties of the coating results. Where in Specimen A the surface
faces directly with the anode and Specimen B the surface accompanies the anode and
tests the thickness, roughness, corrosion resistance.
The best and thickest thickness results were obtained in specimen segment A 1
with a thickness value of 27,91 μm, compared with thickness of specimen B segment 1
with a thickness value of 19,89 μm. In the immersion position with the surface
specimen variation facing directly with the anode has a very high roughness value
with an average value of 2,08 μm compared with the immersion variation on the
surface of the specimen accompanying the anode has a relatively smaller roughness
value with an average value of 1,07 μm . Corrosion resistance that occurs in Adjuster
Chain has the same percentage of corrosion resistance that is equal to 2% of both
variations. By using different variations of immersion, there is no effect on corrosion
resistance. | en_US |
| dc.publisher | FAKULTAS TEKNIK UNIVERSITAS MUHAMMADIYAH YOGYAKARTA | en_US |
| dc.subject | Electroplating, Adjuster Chain, testing | en_US |
| dc.title | PENGARUH PENGATURAN POSISI PENCELUPAN TERHADAP PERSEBARAN PELAPISAN NICKEL-CHROM DALAM PROSES ELECTROPLATING ADJUSTER CHAIN | en_US |