| dc.contributor.advisor | WISNUJATI,ANDIKA | |
| dc.contributor.author | HAFIZ, LALUALPAN | |
| dc.date.accessioned | 2017-01-10T07:34:52Z | |
| dc.date.available | 2017-01-10T07:34:52Z | |
| dc.date.issued | 2016-09-02 | |
| dc.identifier.uri | http://repository.umy.ac.id/handle/123456789/8016 | |
| dc.description | Aluminium merupakan logam ringan yang mempunyai sifat
ketahanan korosi dan mempunyai alir yang baik sehingga banyak digunakan
dalam aplikasi alat-alat rumah tangga, otomotif maupun industri saat ini.
Aluminium paduan pada penelitian ini menggunakan campuran Aluminium
profil dan piston bekas. Piston bekas digunakan untuk mendapatkan unsur Si
yang cukup tinggi pada piston. Penambahan unsur TiB (Titanium-Boron)
sebanyak 0,02% dan perlakuan memberikan tekanan 10 Kg pada saat
pengecoran diharapkan mampu memperbaiki sifat-sifat mekanis dan fisis
Aluminium sehingga diharapkan Aluminium paduan ini memiliki kekuatan
yang jauh lebih baik dibandingkan tanpa perlakuan apapun. Paduan
Aluminium akan dicor pada 2 jenis variasi suhu cetakan sehingga dengan
perlakuan panas terhadap cetakan (dies) yaitu 200oC, dan300oC, diharapkan
mampu memperbaiki sifat getas yang ada pada aluminium.
Pengujian yang dilakukan untuk mengetahui sifat-sifat mekanis
paduan aluminium tersebut yaitu pengujian tarik (Tensile Strngth), dan
komposisibahan. Hasil dari 2 (dua) pengujian tersebut diharapkan mampu
dianalisa sebagai kesimpulan dari penelitian ini. Hasil dari nilai rata-rata uji
tarik pada penelitian ini adalah untuk Raw Material dengan nilai rata-rata
2,33 % , Ti-B 200ºC dengan nilai rata-rata 2,36 % dan Ti-B 300ºC dengan
nilai rata-rata 2,33 %. | en_US |
| dc.description.abstract | Aluminium is a lightweight metal that has properties of corrosion
resistance and has a good flow so vast applications in household appliances,
automotive and industry today. Aluminium alloys in this study using a mixture of
aluminum profiles and former piston. Piston ex used to get high enough Si
element on the piston. The addition of TiB element (Titanium-Boron) of 0.02%
and a treatment pressure of 10 kg at the time of casting is expected to improve the
mechanical properties and physical so hopefully Aluminium, Aluminium alloys
has a strength that is much better than without any treatment. Aluminium alloy
will be cast on two types of variations in temperature of the mold so that the heat
treatment of the molds (dies), namely 200ºC and 300ºC, is expected to improve
the brittle nature of existing on aluminum.
Tests were done to determine the mechanical properties of the aluminum
alloy namely tensile test (Tensile Strngth), and the composition of the material.
Results from the two (2) testing is expected to be analyzed as the conclusions of
this study. The results of the average value of a tensile test on this study was to
Raw Material with an average value of 2.33%, Ti-B 200ºC with an average value
of 2.36% and Ti-B 300ºC with an average value of 2, 33%. | en_US |
| dc.publisher | D3 UMY | en_US |
| dc.subject | Mechanical Properties, Aluminium, Ti-B, and Heat Treatment. SifatMekanik, Aluminium, Ti-B, danPerlakuanPanas. | en_US |