| dc.contributor.advisor | Rahman, Budi Nur | |
| dc.contributor.advisor | Sunardi | |
| dc.contributor.author | ANGGARA, BAYU | |
| dc.date.accessioned | 2018-02-07T06:02:22Z | |
| dc.date.available | 2018-02-07T06:02:22Z | |
| dc.date.issued | 2017-12-28 | |
| dc.identifier.uri | http://repository.umy.ac.id/handle/123456789/17510 | |
| dc.description | Material plastik pada saat ini banyak digunakan dibidang industri, bidang
teknik, maupun untuk penelitian. Banyaknya penggunaan material plastik pada
saat ini dikarenakan plastik mempunyai sifat unggul seperti material yang tahan
korosi, ringan dan harga relatif murah. Namun material tersebut masih
mempunyai beberapa kekurangan. Untuk mengatasi kekurangan dan
meningkatkan kualitasnya plastik salah satunya metode yang digunakan yaitu
pelapisan nikel dengan metode Elektroless plating.
Proses elektroless nikel pada penelitian ini mengunakan plastik
Acrylonitrile Butadiene Styrene (ABS) dengan logam pelapis nikel. Untuk
mendapatkan hasil yang lebih maksimal, variasi yang digunakan pada penelitian
ini adalah waktu aktivasi katalis palladium 4, 6, 8, 10, dan 12 menit dan penelitian
ini menganalisa waktu aktivasi palladium pada plastik Acrylonitrile Butadiene
Styrene (ABS) terhadap sifat fisik dan mekanik lapisan dengan melakukan
pengujian kekerasan, keausan, kekasaran, dan ketebalan lapisan yang dihasilkan
dari tahap electroless pada spesimen.
Pada proses elektroless nikel dengan variasi waktu aktivasi palladium
didapat kekerasan dan ketebalan cenderung meningkat. Sedangkan kekasaran dan
keausan menurun. Berdasarkan penelitian spesimen dengan hasil terbaik diperoleh
pada waktu aktivasi 12 menit dengan nilai kekasaran 0,556 μm, ketebalan 2,84
μm, kekerasan 84,5 SHN dan keausan 0.232 cm2/Kg. | en_US |
| dc.description.abstract | Plastic materials are currently widely used in industry, engineering, and
research. The large number of plastic material use today because plastic has
superior properties such as material that is corrosion resistant, lightweight and
relatively cheap price.But the material still has some drawbacks. To overcome the
deficiencies and improve the quality of plastic, surface treatment can be done by
coating them with electroless nickel plating method.
The electroless Nickel plating process in this research uses Acrylonitrile
Butadiene Styrene (ABS) plastic as a substrate an nickel as coating layer. To
obtain maximum results, the variations used in this study were palladium with
catalyst activation time 4, 6, 8, 10, and 12 minutes. This study analyzed palladium
activation time on Acrylonitrile Butadiene Styrene (ABS) plastic to the physical
and mechanical properties of the coating layer by testing hardness, wear, surface
roughness, and coating thickness resulting from the electroless stage of the
specimen.
In the electroless Nickel plating process with variation of palladium
activation time obtained hardness and thickness tends to increase. While the
roughness and wear tend to decreased. Based on this research, the specimen with
best result obtained at activation time 12 minute with roughness value 0,556 μm,
thickness 2,84 μm, hardness 84,5 SHN and wear 0,232 cm2 / Kg. | en_US |
| dc.publisher | FAKULTAS TEKNIK UMY | en_US |
| dc.subject | Electroless Nickel Plating, Plastic (ABS), Palladium Activation Time. Electroless Nikel, Plastik (ABS), Waktu Aktivasi Palladium. | en_US |
| dc.title | PENGARUH VARIASI WAKTU AKTIVASI KATALIS PALLADIUM PELAPISAN NIKEL TERHADAP KARAKTERISTIK FISIK DAN MEKANIK PADA PLASTIK ABS DENGAN METODE ELEKTROLESS PLATING | en_US |
| dc.type | Thesis
SKR
F T
027 | en_US |