| dc.description | Stuktur yang berpengaruh dalam kontruksi bangunan salah satunya adalah beton.
Banyak para peneliti yang mengganti campuran pembuatan beton dengan bahan material yang di
hasilkan dari limbah, seperti limbah ban, limbah plastik, dan lain-lain. Pemanfaatan campuran
beton menggunakan limbah ban bekas bermaksud dapat mengurangi dan membatasi perusakan
sistematis alam. Penelitian ini menerapkan penggunaan limbah karet ban sebagai pengganti
agregat halus untuk mendapatkan hasil kuat lentur dengan variasi serutan ban 0 %, 5 %,10 %, 15
%, dan 20 % pada beton fc’ 35 MPa dan fc’ 17 MPa. Hasil penelitian menunjukkan bahwa nilai
kuat lentur balok dengan kadar serutan karet ban bekas sebesar 0 %, 5 %,10 %, 15 %, dan 20 %
berturut-turut untuk beton 35 MPa adalah 4,721 MPa, 4,702 MPa, 3,784 MPa, 2,735 MPa, 2,449
MPa. Sedangkan untuk beton 17 MPa adalah 4,112 MPa, 2,306 MPa, 2,054 MPa, 1,800 MPa,
1,003 MPa. Berdasarkan analisis kuat lentur terhadap beton mutu fc’ 35 MPa dan fc’ 17 MPa dapat
dikatakan bahwa penggunaan serutan karet ban sebagai pengganti agregat halus dapat digunakan
namun lebih baik jika digunakan pada beton mutu fc’ 35 MPa dengan variasi serbuk ban sebanyak
5 %. | en_US |
| dc.description.abstract | The structure that affects building construction is concrete. Many researchers are
replacing concrete mixtures with materials produced from waste, such as tire waste, plastic waste,
and others. The use of concrete mixtures using used tire waste is intended to reduce and limit the
systematic destruction of nature. This study applies the use of tire rubber waste as a fine aggregate
substitute to obtain the results of flexural strength with variations in rubber tire crumb 0%, 5%,
10%, 15%, and 20% in fc '35 MPa and fc' 17 MPa concrete. The results showed that the beam
flexural strength with used rubber rubber shavings was 0%, 5%, 10%, 15%, and 20% respectively
for 35 MPa concrete was 4.721 MPa, 4.702 MPa, 3.784 MPa, 2.735 MPa, 2,449 MPa. While for
the 17 MPa concrete is 4.112 MPa, 2.306 MPa, 2.054 MPa, 1,800 MPa, 1.003 MPa. Based on the
flexural strength analysis of fc '35 MPa and fc' 17 MPa quality concrete it can be said that the use
of tire rubber shavings as a substitute for fine aggregates can be used but better if used on fc '35
MPa quality with a variation of 5% rubber tire crumb. | en_US |
| dc.publisher | FAKULTAS TEKNIK UNIVERSITAS MUHAMMADIYAH YOGYAKARTA | en_US |
| dc.subject | concrete, flexural strength, rubber tire crumb, and variety | en_US |
| dc.title | PENGARUH PENGGANTIAN AGREGAT HALUS DENGAN SERUTAN KARET BAN BEKAS PADA KUAT LENTUR BETON | en_US |
| dc.type | Thesis | en_US |